Effect of Ceramic Thickness on the Bond Strength to Resin-Luting Agents before and after Thermal Cycling

Abstract This study investigated microshear bond strength (µSBS) of two (2) dual-cured resin-luting agents (RelyX™ Ultimate and RelyX™ U200) when photoactivated through varying thicknesses of lithium disilicate, with or without thermal cycling. Discs of IPS e.max Press of 0.5, 1.5, and 2 mm in thickness were obtained. Elastomer molds (3.0 mm in thickness) with four cylinder-shaped orifices 1.0 mm in diameter, were placed onto the ceramic surfaces and filled with resin-luting agents. A Mylar strip, glass plate, and load of 250 grams were placed over the filled mold. The load was removed and the resin-luting agents were photoactivated through the ceramics using a single-peak LED (Radii Plus.) All samples were stored in distilled water at 37oC for 24 h. Half of the samples were subjected to thermal cycling (3,000 cycles; 5ºC and 55ºC). All samples were then submitted to µSBS test using a universal testing machine (Instron 4411) at a crosshead speed of 0.5 mm/min. Data were submitted to three-way ANOVA and Tukey post-hoc test (α=0.05). The mean µSBS at 24 h was significantly higher than after thermal cycling (p<0.05). No statistical difference was found between resin-luting agents (p > 0.05). The mean µSBS for groups photoactivated through 0.5 mm ceramic were significantly higher than 1.5 mm and 2.0 mm (p < 0.05). In conclusion, increased ceramic thicknesses reduced the bond strength of tested resin-luting agents to lithium disilicate. No differences were found between resin-luting agents. Thermal cycling reduced the bond strength of both resin-luting agents.

Resumo: Este estudo investigou a resistência de união ao microcisalhamento (RUµC) de dois (2) agentes de cimentação de resina dual (RelyX™ Ultimate e RelyX™ U200) quando fotoativados através de diferentes espessuras de dissilicato de lítio, com ou sem ciclagem térmica. Discos do IPS e.max Press de 0,5, 1,5 e 2 mm de espessura foram obtidos. Moldes de elastômero (3,0 mm de espessura) com quatro orifícios cilíndricos de 1,0 mm de diâmetro foram colocados sobre as superfícies cerâmicas e preenchidos com agentes de cimentação de resina. Uma tira Mylar, placa de vidro e carga de 250 gramas foram colocadas sobre o molde preenchido. A carga foi removida e os agentes de cimentação resinosos foram fotoativados através da cerâmica usando um LED de pico-único (Radii Plus). Todas as amostras foram armazenadas em água deionizada a 37oC por 24 h. Metade das amostras foi submetida a ciclagem térmica (3.000 ciclos; 5ºC e 55ºC). Todas as amostras foram então submetidas ao teste de RUµC usando uma máquina de teste universal (Instron 4411) com velocidade de 0,5 mm/min. Os dados foram submetidos à Análise de Variância três fatores e ao teste post-hoc de Tukey (α = 0,05). A média de RUµC em 24 h foi significativamente maior do que após a ciclagem térmica (p < 0,05). Não houve diferença estatística entre os cimentos resinosos (p > 0,05). As médias de RUµC para grupos fotoativados através de cerâmica de 0,5 mm foram significativamente maiores do que 1,5 mm e 2,0 mm (p < 0,05). Em conclusão, o aumento da espessura da cerâmica reduziu a resistência de união dos agentes de cimentação resinosos ao dissilicato de lítio. Não foram encontradas diferenças entre os agentes de cimentação resinosos. A ciclagem térmica reduziu a resistência de união de ambos os agentes de cimentação resinosos.

Surface Analysis of a Universal Resin Composite and Effect of Preheating on its Physicochemical Properties

Abstract This study was aimed at analyzing the surface properties of a universal resin composite and evaluating the effect of preheating on its physicochemical properties. Two commercial resin composites were used under two conditions: Filtek Universal Restorative (UR); UR preheated (URH); Filtek Supreme (FS) and FS preheated (FSH). The film thickness (FT) test (n = 10) was done using two glass slabs under compression. Flexural strength (FLS) and modulus (FLM) were evaluated using a three-point flexion test (n = 10). Polymerization shrinkage stress (PSS) was evaluated in a universal testing machine (n = 5). Gap width (GW) between composite and mold was measured in internally polished metallic molds (n = 10). The degree of conversion (DC) was evaluated by Fourier Transform Infrared spectroscopy (n = 3). The morphology of the filler particles was checked by scanning electron microscope (SEM) and EDX analysis. Surface gloss (SG) and surface roughness (SR) were evaluated before and after mechanical brushing (n = 10). The outcomes were submitted to 2-way ANOVA and Tukey's test (α = 0.05). Lower mean values of FT were observed for the preheated groups when compared to the non-preheated groups. URH and FSH showed higher mean values of FLS and FLM when compared with UR and FS. No differences were observed between groups in the PSS test. The GW was higher for the UR and FS groups when compared with URH and FSH. The DC was higher for preheated resin composites when compared to the non-preheated groups. The SR of the UR composite was higher than the FS after mechanical brushing, while the SG was higher for the FS groups. In conclusion, the universal resin composite tested generally presented similar physicochemical properties compared with the nanofilled resin composite and either similar or slightly inferior surface properties. The preheating improved or maintained all properties evaluated.

Resumo Neste estudo avaliou-se propriedades físico-químicas e de superfície de um compósito universal pré-aquecido e comparado a um compósito convencional. Foram utilizados dois compósitos comerciais: Filtek Universal Restorative (UR); UR pré-aquecido (URH); Filtek Supreme (FS) e FS pré-aquecido (FSH). O teste de espessura de película (EP) (n = 10) foi feito usando duas placas de vidro sob compressão. A resistência à flexão (RF) e o módulo flexural (MF) foram avaliados por meio do teste de flexão de três pontos (n = 10). A tensão de contração de polimerização (TCP) foi avaliada em uma máquina de teste universal (n = 8). A largura da fenda (LF) entre o compósito e o molde foi medida em moldes metálicos polidos internamente (n = 10). O grau de conversão (GC) foi avaliado por espectroscopia de infravermelho com transformada de Fourier (n = 3). A morfologia das partículas de carga foi observada em microscopia eletrônica de varredura (MEV) e sua composição em EDX. Brilho superficial (BS) e rugosidade superficial (RS) foram avaliados antes e após escovação mecânica (n=10). Os resultados foram submetidos à ANOVA 2-fatores e as médias comparadas pelo teste de Tukey (α = 0,05). Menores valores médios de EP foram observados para os grupos pré-aquecidos quando comparados aos grupos não pré-aquecidos. URH e FSH apresentaram maiores valores médios de RF e MF quando comparados com UR e FS. Não foram observadas diferenças entre os grupos no teste TCP. A LF foi maior para os grupos UR e FS quando comparados com URH e FSH. O GC foi maior para os compósitos pré-aquecidos quando comparados aos não pré-aquecidos. A RS do compósito UR foi maior que o FS após a escovação mecânica, enquanto o BS foi maior para os grupos FS. Em conclusão, o compósito universal testado geralmente apresentou propriedades físico-químicas semelhantes em comparação ao compósito nanoparticulado e propriedades de superfície semelhantes ou ligeiramente inferiores. O pré-aquecimento melhorou ou manteve todas as propriedades avaliadas.

Does the initial surface roughness of different CuNiTi wires affect the frictional resistance?

Abstract This study aimed to assess and correlate initial surface roughness and frictional resistance of rectangular CuNiTi wires inserted in different self-ligating brackets. The sample consisted of 40 bracket-wire sets (rectangular CuNiTi wires of 0.017" x 0.025" and passive self-ligating brackets) divided into four groups (n=10): metallic self-ligating bracket and metallic CuNiTi wire (G1); metallic self-ligating bracket and rhodium-coated CuNiTi wire (G2); esthetic self-ligating bracket and metallic wire (G3); esthetic self-ligating bracket and rhodium-coated CuNiTi wire (G4). The initial surface roughness of the wires was examined with a Surfcorder roughness meter, model SE1700. Later, frictional resistance was assessed in an Instron 4411 universal testing machine at a speed of 5 mm/min, in an aqueous medium at 35°C. Microscopic analyses of surface morphology were performed with scanning electron microscopy, using an LEO 1430, with magnifications of 1000X. Generalized linear models were applied, considering the 2 x 2 factorial (bracket type x wire type), at a 5% significance level. Regardless of bracket type, the groups with esthetic wires presented higher initial surface roughness than the groups with metallic wires (p<0.05). There was no significant difference between the different bracket-wire sets for frictional resistance and no significant correlation between frictional resistance and initial surface roughness in the environment studied. It is concluded that esthetic wires presented higher initial surface roughness but did not interfere with the frictional resistance between brackets and wires.

Resumo O objetivo deste estudo foi avaliar e correlacionar a rugosidade superficial inicial e a resistência a fricção dos fios CuNiTi retangulares inseridos em diferentes bráquetes autoligados. A amostra foi composta por 40 conjuntos bráquetes-fios (fios retangulares CuNiTi de 0.017" x 0.025" e braquetes autoligados passivos), divididos em 4 grupos (n=10): bráquete autoligado metálico e fio CuNiti metálico (G1); braquete autoligado metálico e fio CuNiti com revestimento de rhodium (G2); bráquete autoligado estético e fio metálico (G3); bráquete autoligado estético e fio CuNiti com revestimento de rhodium (G4). A rugosidade superficial inicial do fio foi examinada com um rugosímetro Surfcorder modelo SE1700. Posteriormente, a resistência a fricção foi avaliada em uma máquina de ensaios universal Instron 4411, a uma velocidade de 5mm/min em meio aquoso à 35oC. Análises microscópicas da morfologia de superfície foram realizadas por microscopia eletrônica de varredura, utilizando um LEO 1430, com ampliações de 1000X. Foram aplicados modelos lineares generalizados, considerando o fatorial 2 x 2 (tipo de bráquete x tipo de fio), com o nível de significância de 5%. Independentemente do tipo de bráquete, os grupos com fios estéticos apresentaram maior rugosidade superficial inicial que os grupos com fios metálicos (p<0,05). Não houve diferença significativa entre os diferentes conjuntos bráquetes-fios quanto a resistência à fricção e não houve correlação significativa entre a resistência a fricção e a rugosidade superficial inicial no ambiente estudado. Conclui-se que os fios estéticos apresentaram maior rugosidade superficial inicial porém não interferiram na resistência a fricção entre os braquetes e os fios.

Bond strength of different orthodontic brackets produced with different materials and fabrication methods / Resistência de união de bráquetes ortodônticos produzidos com diferentes materiais e métodos de fabricação

Objective: The aim of this study was to evaluate the effects of material and processing methods on the bond strength of orthodontic brackets. Material and Methods: Five types of brackets were tested: Conventional metallic (CM), metallic sandblasted (SB), ceramic (C), polycarbonate (PC), and metallic fabricated by melting injection molding (MIM). Shear bond strength (SBS) was conducted to check bond strength of the brackets bonded to bovine teeth (n=10/group), and tensile bond strength (TBS) (20 brackets/group) to check bracket retention to bonding material (n=20/group). Both, SBS and TBS were conducted with 1mm/min crosshead speed in a universal testing machine. Bond strength was calculated in Megapascal (MPa) based on force (N) and bracket area (mm 2). Data normality was verified, and One-way ANOVA was the statistical test with Tukey post-hoc (α=0.05). Results: SB and MIM presented higher SBS compared to C, PC, and CM (p<0.05). SB and MIM also presented significantly higher TBS compared to CM and PC (p<0.05). However, MIM was not different of C for TBS. Conclusion: The type of material and method of fabrication are determinant factors that affect bond strength of orthodontic brackets and melting injection molding (MIM) is a remarkable technology to improve brackets retention during the orthodontic treatment. (AU)

Objetivo: O objetivo deste estudo foi avaliar os efeitos dos materiais e métodos de processamento na resistência de união de bráquetes ortodônticos. Material e Métodos: Cinco tipos de bráquetes foram testados: Convencionais metálicos (CM), metálicos jateados (SB), cerâmico (C), policarbonato (PC), e metálico fabricado por injeção de metal fundido em molde (MIM). A resistência de união ao cisalhamento (SBS) foi conduzida para verificar a resistência de união dos bráquetes aderidos a dentes bonivos (n=10/grupo) e a resistência à tração (TBS) (20 bráquetes/grupo) para verificar a retenção do bráquete ao material adesivo (n=20/grupo). SBS e TBS foram conduzidas com relação carga/velocidade de 1mm/min em uma máquina de ensaios universal. A resistência de união foi calculada em Megapascal (MPa) com base na força (N) pela área do bráquete (mm 2). A normalidade dos dados e a estatística foi realizada utilizando One-way ANOVA e Tukey post-hoc (α=0.05). SB e MIM apresentaram os maiores valores de SBS comparados com C, PC e CM (p<0.05). Resultados: SB e MIM também apresentaram valores significativamente maiores de TBS comparados com CM e PC (p<0.05). Contudo, os valores de TBS para o grupo MIM não foram significativamente diferentes de C. Conclusão: O tipo de material e o método de fabricação são fatores determinantes que afetam a resistência de união de bráquetes ortodônticos e a injeção de metal fundido em molde (MIM) é uma tecnologia relevante para melhorar a retenção dos bráquetes durante o tratamento ortodôntico. (AU)

Do dual-cure bulk-fill resin composites reduce gaps and improve depth of cure

Abstract This in vitro study aimed to evaluate the gaps length and depth of cure of dual-cure bulk-fill resin composites inserted in box-shaped preparations. Box-shaped preparations (4 mm deep) were made in fifteen human third-molars and divided into three groups according to the resin composites (n=5): Dual-cure bulk-fill BulkEZ (BEZ); Dual-cure bulk-fill HyperFIL (HF); and Tetric Evoceram Bulk-fill (TETRIC), as control. Gaps length (%) was evaluated in tooth-restoration interface with micro-computed tomography (µCT). The restorations were sectioned, and the degree of conversion (DC) and Knoop microhardness were evaluated at five depths (0.3, 1, 2, 3, and 4 mm). Microhardness data were statistically evaluated using absolute values (KHN) and relative values (microhardness percentages in relation to top). Gaps length (%) increased in the following order: BEZ=TETRIC<HF. The microhardness percentages in relation to top significantly decreased from 2 mm for TETRIC and 3 mm for HF. BEZ had constant microhardness and DC at all depths, while HF and TETRIC presented a significant decrease on DC at 4 mm. Dual-cure bulk-fill composites did not reduce gaps compared to light-cure bulk-fill, but they can improve depth of cure of bulk-filled restorations.

Resumo O objetivo neste estudo in vitro foi mensurar as fendas e a profundidade de polimerização de compósitos resinosos bulk-fill duais inseridos em preparos em forma de caixa. Os preparos em forma de caixa (4 mm de profundidade) foram realizados em quinze terceiros molares e separados em 3 grupos, de acordo com o compósito resinoso (n = 5): Bulk-fill dual BulkEZ (BEZ); Bulk-fill dual HyperFIL (HF); Tetric Evoceram Bulk-fill (TETRIC). O comprimento das fendas (%) foi avaliado na interface dente-restauração por meio de micro-tomografia computadorizada (µCT). As restaurações foram seccionadas e o grau de conversão (GC) e microdureza Knoop foram avaliados em cinco profundidades (0,3, 1, 2, 3 e 4 mm). Os dados de microdureza foram avaliados estatisticamente por meio de valores absolutos e relativos (porcentagens de microdureza em relação ao topo). O comprimento das fendas (%) aumentou na seguinte ordem: BEZ = TETRIC <HF. O percentual de microdureza em relação ao topo diminuiu significativamente a partir de 2 mm para TETRIC e 3 mm para HF. BEZ apresentou percentuais de microdureza e de GC constantes em todas as profundidades, enquanto HF e TETRIC apresentaram decréscimo significativo no GC em 4 mm. Os compósitos resinosos bulk-fill duais não reduziram as fendas formadas quando comparados a um compósito bulk-fill fotopolimerizável; entretanto, os mesmos podem melhorar a profundidade de polimerização em restaurações de incremento único.

Force degradation of elastomeric chains after storage time and mechanical brushing

Abstract The purpose of this in vitro study was to evaluate the force decrease of different elastomeric chains after different times: initial, 10 minutes, 1 day, 28 days and after mechanical brushing. Twenty orthodontic elastomeric chains segments were utilized for each commercial brand. Initially, the elastomeric chain of 15mm long were immediate stretched up to 20 mm in an Instron and the force was measured in gf. After all specimens were placed stretched on rectangular acrylic jigs with distance of 20 mm, immersed in deionized water at 37oC for 10 minutes and the force (gf) was measured again. Five test measurements of remaining force were made at the following time intervals: initial, 10 minutes, 1 day, 28 days and mechanical brushing. After 28 days, the acrylic plates with the specimens were adapted in the mechanical brushing machines (MSCT 3) and the elastomeric chains were submitted to mechanical brushing and the force (gf) measure again. The force (gf) was submitted to mixed-model ANOVA and Sidak post-hoc test (α=0.05). A statistically significant reduction in the force was found for all orthodontic elastomeric chain types after 1 day, 28 days and mechanical brushing (p<0.05). Morelli and 3M Unitek elastomeric chains showed significantly higher force than Abzil and GAC (p<0.05) after 1 day, 28 days and mechanical brushing. In conclusion, the force delivered by all elastomeric chains decayed rapidly over time. Morelli and 3M Unitek elastomeric chains consistently had a significantly greater force after mechanic brushing, while GAC the lowest.

Resumo O objetivo deste estudo in vitro foi avaliar a redução da força de diferentes cadeias elastoméricas após diferentes tempos: inicial, 10 minutos, 1 dia, 28 dias e após escovação mecânica. Vinte segmentos de cadeias elastoméricas ortodônticas foram utilizadas para cada marca comercial. Inicialmente, a cadeia elastomérica de 15 mm de comprimento foi esticada imediatamente até 20 mm na Instron e a força foi medida em (gf). Após, todas as amostras foram adaptadas esticadas em placas retangulares de acrílico na distância de 20 mm, imersas em água deionizada a 37o C por 10 minutos e a força (gf) foi medida novamente. Cinco medidas de força foram feitas nos seguintes intervalos de tempo: inicial, 10 minutos, 1 dia, 28 dias e após a escovação mecânica. Após 28 dias, as placas de acrílico com as amostras foram adaptadas na máquina de escovação (MSCT 3) e as cadeias elastoméricas foram submetidas a escovação mecânica e a medida de força (gf) novamente. Os dados da força (gf) foram submetidos a ANOVA modelo misto e teste post-hoc de Sidak (α = 0,05). Uma redução estatisticamente significativa na força foi encontrada para todos os tipos de cadeia elastomérica ortodôntica após 1 dia, 28 dias e escovação mecânica (p<0,05). As cadeias elastoméricas Morelli e 3M Unitek apresentaram força significativamente superior em relação a Abzil e GAC (p<0,05) após 1 dia, 28 dias e escovação mecânica. Em conclusão, a força distribuída por todas as cadeias elastoméricas decaiu rapidamente com o tempo. As cadeias elastoméricas Morelli e 3M Unitek consistentemente tiveram uma força significativamente maior após a escovação mecânica, enquanto GAC a mais baixa.

CHX stabilizes the resin/demineralized dentin interface

Abstract The aim of this study was to evaluate the effect of 2% chlorhexidine digluconate (CHX) on microtensile bond strength (µTBS) between an adhesive system and under 3 dentin conditions. For that, this study evaluated the adhesive interface at initial, after 6 months and 1 year of storage. Forty-eight human third molars were prepared and randomly divided into 3 groups, according to dentin substrates: sound dentin (Sd), caries-infected dentin (Ci) and caries-affected dentin (Ca). The groups were subdivided into two according to the dentin pre-treatment: application of 2% CHX or without pre-treatment (control). The dentin surfaces were etched with 35% phosphoric acid gel and bonded with Adper Single Bond 2 (3M ESPE) adhesive system according to manufacturer's instructions. Subsequently, the specimens were stored in deionized water at 37°C for 24h, 6 months and 1 year. Two additional teeth were used to analyze the bonding interfaces by SEM. Data was submitted to three-way ANOVA in a split plot design and Tukey's test (α = 0.05). The results showed that Ci decreased µTBS values when compared to Ca and Sd, regardless storages time or treatment. Stored samples for 6 months and 1 year decreased the µTBS for the control group, but no difference was found between storages time for the CHX group. As a conclusion, the 2% CHX application after etching showed improved dentin bond strength in the storage time, regardless of the substrates evaluated.

Resumo O objetivo deste estudo foi avaliar o efeito do digluconato de clorexidina 2% (CHX) na resistência de união à microtração (µTBS) entre um sistema adesivo e sob 3 condições de dentina. Para tanto, este estudo avaliou a interface adesiva no início, após 6 meses e 1 ano de armazenamento. Quarenta e oito terceiros molares humanos foram preparados e divididos aleatoriamente em 3 grupos, de acordo com os substratos dentinários: dentina hígida (Dh), dentina infectada por cárie (Di) e dentina afetada por cárie (Da). Os grupos foram subdivididos em dois de acordo com o pré-tratamento: aplicação de CHX 2% ou sem pré-tratamento (controle). As superfícies da dentina foram condicionadas com gel de ácido fosfórico a 35%, em seguida, utilizou-se o sistema adesivo Adper Single Bond 2 (3M ESPE) de acordo com as instruções do fabricante. Posteriormente, os corpos-de-prova foram armazenados em água deionizada a 37°C por 24h, 6 meses e 1 ano. Dois dentes adicionais foram usados ​​para analisar as interfaces de união no MEV. Os dados foram submetidos a ANOVA três fatores em esquema de parcela subdividida e ao teste de Tukey (α = 0,05). Os resultados mostram que a Di diminuiu os valores de µTBS quando comparado as Da e Dh, independente do tempo de armazenamento ou tratamento. Amostras armazenadas por 6 meses e 1 ano diminuíram a µTBS para o grupo de controle, mas nenhuma diferença foi encontrada entre o tempo de armazenamento para o grupo CHX. A aplicação de CHX 2% após o condicionamento apresentou melhora na resistência de união à dentina no tempo de armazenamento, independente dos substratos avaliados.

Effect of combining photoinitiators on cure efficiency of dental resin-based composites

Abstract Camphorquinone is the most conventionally used photoinitiator in Dentistry. Although different alternative photoinitiators have been proposed, no photoinitiator was capable of completely substituting camphorquinone. The combination of photoinitiators has been considered the best alternative. Objectives: To evaluate the effect of combining Norrish type I and II photoinitiators on the cure efficiency of dental resin-based composites. Methodology: Experimental composites were produced containing different photoinitiator systems: Norrish type I-only, mono-alkyl phosphine oxide (TPO); Norrish type II-only, camphorquinone (CQ); or its combination, CQ and TPO, in a 1: 1 molar ratio. UV-vis absorption spectrophotometry was performed to assess the consumption of each photoinitiator after curing (n=3). A multi-wave LED (Bluephase® G2, Ivoclar Vivadent) was pre-characterized and used with a radiant exposure of 24 J/cm2. The degree of conversion was evaluated by Raman spectrometry, and the elution of the monomers by nuclear magnetic resonance analysis (n=3). Data were analyzed using ANOVA and Tukey's test (α=0.05; β=0.2). Results: The combination of CQ and TPO increased the consumption of the photoinitiator system compared to CQ-only (p=0.001), but presented similar consumption compared to TPO-only (p=0.52). There was no significant difference in the degree of conversion between the composites regardless of the photoinitiator system (p=0.81). However, the elution of the monomers was reduced when both photoinitiators were combined. TPO-based material presented the highest elution of monomers. Conclusions: The combination of the photoinitiator systems seems to be beneficial for the cure efficiency of dental resin-based composites.

Evaluation of friction on self-ligating and conventional brackets associated with different types of archwires submitted to sliding mechanics

Aim: The aim of this study was to verify the frictional force during sliding mechanics in orthodontic tooth movement, using conventional metal brackets of the active and passive self-ligating types with stainless steel and copper nickel titanium archwires. Methods: This experimental in vitro study was conducted with conventional metal (Morelli, Sorocaba, SP, Brazil) brackets, active self-ligated (SLI Morelli, Sorocaba, SP, Brazil) and passive self-ligated (SLP Morelli, Sorocaba, SP, Brazil), with slot 0.022 x 0.028 inches and Roth prescription. The brackets were tested with rectangular section 0.019 x 0.025 inch copper nickel titanium and stainless steel archwires. For each type of bracket, 10 sets of plate/bracket/archwire segment (n=10) were fabricated. Non-parametric Kruskal Wallis and Dunn tests were used for comparison between types of brackets and Wilcoxon tests for comparison between types of archwires. Results: The results showed that the frictional force values were higher with copper nickel titanium than with stainless steel archwires (p<0.05). When copper nickel titanium archwires were used, the active self-ligating brackets showed higher frictional force values than the other types, followed by the conventional brackets. Lower frictional force values were observed with passive self-ligating brackets. For stainless steel archwires, no difference was observed between conventional and active self-ligating brackets, the passive self-ligating type presented lower frictional force values than the others. Conclusion: It was concluded that the higher frictional force was observed when active self-ligating brackets were associated with copper nickel titanium archwires. Lower frictional force was verified between passive self-ligating brackets combined with stainless steel archwires

Evaluation of degradation of force of esthetic elastomeric chains / Avaliação da degradação de força de correntes elastoméricas estéticas

Abstract Introduction Elastomers are considered important allies to orthodontic treatment and due to the aesthetic demand, aesthetic elastomers are increasingly used in adult patients. Objective The aim of this experimental in vitro study was to evaluate the degradation of force of esthetic elastomeric chains, of three different sizes: short, medium and long. Material and method For evaluating the degradation of force, 90 elastomeric chain segments were used, divided into 9 Groups (n=10), as follows: Morelli short elastomer, Morelli medium, Morelli long, Orthometric short, Orthometric medium, Orthometric long, American Orthodontic short, American Orthodontic medium and American Orthodontic long. Acrylic plates with pins were used to provide stretching of the elastomeric chains. The initial stretching force of the elastomeric chain was 150 grams, measured by a tensiometer. After this, they were prestretched to 50% of their original length, measured in an Instron 4411 Universal test machine, and placed on the seating pin on the plate. The plate was immersed in artificial saliva at 37 °C in a plastic receptacle, and removed for measurement after a time interval of 21 days. For statistical analysis, the methodology of mixed models for repeated measures in time and Tukey-Kramer test were used. Degradation of the forces was analyzed by 2-way analysis of variance (ANOVA) and the Tukey test. Result All the elastomeric chains showed statistically significant reduction in force (p<0.05). The American Orthodontic elastomeric chains showed higher reduction in force values, irrespective of the elastic size (p<0.05). Conclusion The three commercial brands studied underwent significant reduction in the quantity of force released; the American Orthodontic brand of elastomer showed the highest value of degradation in force.

Resumo Introdução Os elastômeros são considerados aliados importantes do tratamento ortodôntico e, devido à demanda estética, os elastômeros estéticos são cada vez mais utilizados em pacientes adultos. Objetivo O objetivo desse estudo experimental in vitro foi avaliar a degradação de forças geradas pelas cadeias elastoméricas estéticas, em três diferentes tamanhos curto, médio e longo. Material e método Para a avaliação da degradação da força foram utilizados 90 segmentos de cadeias elastoméricas, divididos em 9 grupos (n=10), sendo: elastômero Morelli curto, Morelli médio, Morelli longo, Orthometric curto, Orthometric médio, Orthometric longo, American Orthodontic curto, American Orthodontic médio e American Orthodontic longo. Foram utilizadas placas de acrílico com pinos que proporcionaram o estiramento das cadeias elastoméricas. A força inicial de estiramento da cadeia elastomérica foi de 150 gramas, medidas por um tensiômetro. Em seguida foram pré-estiradas em 50% do seu comprimento original, medidas em uma máquina Universal Instron 4411 e levadas ao pino de assentamento na placa. A placa foi imersa em um recipiente plástico com saliva artificial a 37 °C e removida após 21 dias para aferição. Foi aplicada metodologia de modelos mistos para medidas repetidas no tempo e teste de Tukey-Kramer. A degradação das forças foi analisada por análise de variância (ANOVA) "2 fatores" e teste de Tukey. Resultado Todas as correntes elastoméricas apresentaram redução estatisticamente significativa da força (p<0,05). As correntes elastoméricas da American Orthodontic apresentaram maior redução de força, independentemente do tamanho do elástico (p<0,05). Conclusão As três marcas comerciais estudadas sofreram uma redução significativa na quantidade de força liberada, sendo o elastômero da marca American Orthodontic o que apresentou maior degradação de força.

Effect of Ceramic Interposition and Post-activation Times on Knoop Hardness of Different Shades of Resin Cement

Abstract The aim of this study was to evaluate Knoop hardness of different shades of a resin cement light-cured directly or through ceramic discs, measured 15 min or 24 h after light exposure, and at different depths. Specimens of a commercial resin cement (Variolink Veneer) in seven shades, were fabricated in an elastomeric mold, covered with a mylar strip, a 0.7 mm thick ceramic disc (IPS e.max Press) was placed and the cement was light-activated for 20 s using a blue LED (Radii-Cal). The cured resin cement specimens were transversely wet-flattened to their middle portion and microhardness (Knoop) values were recorded at 15 min after light exposure and after deionized water storage at 37 ºC for 24 h. Five indentations were made in the cross-sectional area at 100 and 700 μm depths from the top surface. Ten specimens were made for each test conditions. Data were submitted to ANOVA split-plot design (shade, post-cure time, mode of activation and depth), followed by Tukey post hoc test (α=0.05). Significant differences for shade (p<0.0001), mode of activation (p<0.001), post-cure time (p<0.0001) and depth (p<0.0001) were detected. No significant interactions (p>0.05) were found, except for shade x post-cure time (p<0.0045) and mode of activation x post-cure time (p<0.0003). Resin cement shade has a significant effect on Knoop hardness. Indirect activation through a ceramic material reduced significantly Knoop hardness. Hardness Knoop significantly increased after 24 h in all cements shades compared to values obtained after 15 min. Resin cement depth significantly reduced Knoop hardness.

Resumo O objetivo deste estudo foi avaliar a dureza Knoop de diferentes cores de um cimento resinoso fotoativado diretamente ou através da interposição de um disco de cerâmica, medindo 15 min ou 24 h após exposição à luz, em diferentes profundidades. Amostras do cimento resinoso (Variolink Veneer) em sete cores foram fabricados num molde de elastômero, coberto com tira de poliéster, seguido de um disco cerâmico (IPS e.max Press) com 0.7 mm de espessura e fotoativado por 20 s com o aparelho LED (IPS e.max Press). O cimento resinoso fotoativado foi transversalmente desgastado na porção média e os valores de microdureza Knoop foram obtidos após 15 min após exposição à luz e após armazenagem em água deionizada à 37 °C por 24 h. Cinco penetrações foram feitas na secção transversal à 100 e 700 μm da superfície de topo. Dez amostras foram confeccionadas para cada condição de teste. Os dados foram submetidos à Análise de Variância em esquema de parcelas subdivididas (cor, tempo pós-ativação, modo de ativação e profundidade), seguido pelo teste de Tukey post hoc (α=0,05). Diferença significante para a cor (p<0,0001), modo de ativação (p<0,001), tempo pós-ativação (p<0,0001) e profundidade (p<0,0001) foi detectada. Nenhuma interação significante foi encontrada (p>0,05), exceto para a interação cor x tempo pós-ativação (p<0,0045) e modo de ativação x tempo pós-ativação (p<0,0003). A cor do cimento resinoso teve significante efeito na dureza Knoop. A ativação indireta através do material cerâmico reduziu significativamente a dureza Knoop. A dureza Knoop aumentou significativamente após 24 h em todas as cores do cimento comparados aos valores obtidos após 15 min. A profundidade do cimento resinoso reduziu significativamente os valores de dureza Knoop.

Influence of adhesive and bonding material on the bond strength of bracket to bovine tooth

Aim: To evaluate, in vitro, the effect of adhesive and bonding materials on the shear bond strength (SBS) of metallic brackets bonded to bovine teeth. Methods: Bovine teeth were embedded with acrylic resin, etched with 35% phosphoric acid for 20 s, rinsed, dried for 20 s and divided into 8 groups (n=20), according to the bonding materials and adhesive: Groups 1 and 5 ­ Transbond XT; Groups 2 and 6 ­ Fill Magic; Groups 3 and 7 ­ Biofix; and, Groups 4 and 8 ­ Orthocem. One layer of adhesive 3 M Unitek (Group 1), and one layer of Single Bond Universal Adhesive (Groups 2, 3 and 4) were applied and light-cured with LED for 10 s. Brackets were bonded to the buccal surface with four bonding materials and light-cured with LED for 40 s. SBS was carried out after 24 h and thermocycling (7,000 cycles - 5°/55 °C). Data were submitted to two way ANOVA and Tukey's post hoc test (α=0.05). The Adhesive Remaining Index (ARI) was evaluated at 8×. Results: The adhesive was effective in increasing the SBS for all bonding materials (p<0.05). Significant difference (p<0.05) on the SBS was observed between bonding materials with or without adhesive. The ARI showed a predominance of scores 0 for all groups. Conclusions: The adhesive improved significantly the SBS of the brackets to teeth. Different SBS values occurred among the bonding materials. ARI index showed predominance of score 0 for all groups (AU)

Influence of Thermal Cycles Number on Bond Strength of Metallic Brackets to Ceramic

Abstract The aim of this study was to evaluate the effect of different number of thermal cycles on the shear bond strength (SBS) of metallic orthodontic brackets bonded to feldspathic ceramic by a composite resin. Twenty-five ceramic cylinders were etched with 10% hydrofluoric acid for 60 s and received two layers of silane. Brackets were bonded to the cylinders using Transbond XT and assigned to 5 groups (n=5): Group 1 - Control group (without thermal cycling); Group 2 - 500 thermal cycles; Group 3 - 5,000 thermal cycles; Group 4 - 7,000 thermal cycles and Group 5 - 10,000 thermal cycles. Light-activation was carried out by Radii Plus LED. SBS testing was carried out after 24 h of storage in deionized water and thermal cycling (5/55 oC and 30 s dwell time). Five brackets were bonded to each cylinder, totalizing 25 brackets for each group. Data were submitted to one-way ANOVA and Tukey’s test (α=0.05). The Adhesive Remnant Index (ARI) was evaluated at 8× magnification. The SBS (MPa) of control group (9.3±0.8), 500 (9.0±0.7) and 5,000 (8.4±0.9) thermal cycles were significantly higher than those after 7,000 (6.8±0.6) and 10,000 (4.9±1.0) thermal cycles (p<0.05). The ARI showed a predominance of Scores 0 (adhesive failure) prevailed in all groups, as shown by the ARI, with increased scores 1 and 2 (mixed failures) for control group and 500 thermal cycles. In conclusion, thermal fatigue may compromise the bonding integration between metallic brackets and ceramic restorations. For in vitro testing, use of at least 7,000 cycles is advised to result in significant fatigue on the bonding interface.

Resumo O objetivo neste estudo foi avaliar o efeito de diferentes números de ciclos térmicos na resistência da união de braquetes metálicos à cerâmica feldspática usando resina composta. Vinte e cinco cilindros de cerâmica foram condicionados com ácido fluorídrico a 10% por 60 s e duas camadas de silano. Braquetes foram fixados nos cilindros usando Transbond XT e depois separados em 5 grupos (n=5): Grupo 1 - Grupo Controle (sem ciclagem térmica); Grupo 2 - 500 ciclos térmicos; Grupo 3 - 5.000 ciclos térmicos; Grupo 4 - 7.000 ciclos térmicos e Grupo 5 - 10.000 ciclos térmicos. A fotoativação foi realizada com aparelho LED Radii Plus. O ensaio de resistência de união ao cisalhamento foi realizado após armazenagem por 24 h em água deionizada ou após a ciclagem térmica (5º/55 ºC, com banhos de 30 s cada). Cinco braquetes foram fixados em cada cilindro, totalizando 25 bráquetes por grupo. Os dados foram submetidos à análise de variância de um fator e ao teste de Tukey (α=0,05). O Índice de Remanescente Adesivo (IRA) foi avaliado com aumento de 8x. Os valores de resistência (MPa) dos grupos controle (9,3±0,8), 500 (9,0±0,7) e 5.000 (8,4±0,9) ciclos térmicos foram significantemente maiores do que os grupos submetidos à 7.000 (6,8±0,6) e 10.000 (4,9±1,0) ciclos térmicos (p<0,05). O IRA mostrou predominância do escore 0 para todos os grupos, com aumento de escores 1 e 2 para os grupos controle e submetidos a 500 ciclos térmicos. Em conclusão, a fadiga térmica pode comprometer a união entre os braquetes metálicos e as restaurações cerâmicas. Para testes in vitro, o uso de pelo menos 7.000 ciclos é recomendado para determinar fadiga significante na interface de união.

Deflection and Flexural Strength Effects on the Roughness of Aesthetic-Coated Orthodontic Wires

Abstract The aim was to evaluate the flexural strength and the effects of deflection on the surface roughness of esthetic orthodontic wires. The sample consisted of 70 archwire 0.014-inch: polytetrafluorethylene (PTFE)-coated Nickel-Titanium (Niti) archwires (Titanol Cosmetic-TC, Flexy Super Elastic Esthetic-FSE, esthetic Nickel Titanium Wire-ANT); epoxy resin-coated Niti archwires (Spectra-S, Niticosmetic-TEC); gold and rhodium coated Niti (Sentalloy-STC) and a control group (superelastic Niti (Nitinol-NS). The initial roughness was evaluated with a rugosimeter. After that, the wires were submitted to flexural test in an universal testing machine. Each wire was deflected up to 2 mm at a speed of 1 mm/min. After flexural test, the roughness of the wires was evaluted on the same surface as that used for the initial evaluation. The data of roughness and flexural strength were analyzed by one-way ANOVA and Tukey’s test (a=0.05). Student t-test compared roughness before and after deflection (a =0.05). The roughness of S and ANT (epoxy resin and PTFE-coated wires, respectively), before and after deflection, was significantly higher than the other groups (p<0.05). Wire deflection significantly increased the roughness of the wires S and STC (p<0.05). The flexural strength of groups FSE and NS (PTFE and uncoated) was higher compared with that of the other groups (p<0.05). We concluded that the roughness and flexural strength of the orthodontic wires does not depend on the type of the esthetic coating, but it is influenced by the method of application of this coating. The deflection can increase the roughness of the esthetic orthodontic wires.

Resumo O objetivo foi avaliar a resistência a flexão e os efeitos da deflexão na rugosidade de superfície de fios ortodônticos estéticos. A amostra foi composta por 70 segmentos de fios NiTi calibre 0,014 polegadas: revestidos por politetrafluoretileno (PTFE) (Titanol Cosmetic-TC, Flexy Super Elastic Esthetic-FSE, Aesthetic Nickel Titanium Wire-ANT); revestidos por resina epoxídica (Spectra-S, Niticosmetic-TEC); revestidos por ouro e ródio (Sentalloy-STC); e grupo controle sem revestimento (Nitinol-NS). A rugosidade inicial foi avaliada em perfilômetro. Em seguida, os fios foram submetidos ao teste de resistência a flexão 3 pontos em máquina de ensaio universal. Cada fio foi defletido até 2mm com velocidade de 1 mm/min. Após o ensaio de resistência a flexão, a rugosidade dos fios foi verificada na mesma superfície avaliada inicialmente. Os resultados rugosidade e resistência a flexão foram analisados por análise de variância 1 fator e teste de Tukey (a=0,05). Teste t de Student foi utilizado para comparação da rugosidade antes e após deflexão (a=0.05). A rugosidade de S e ANT (revestimentos resina epoxídica e PTFE, respectivamente), antes e após a deflexão, foi significativamente maior que dos demais grupos (p<0,05). A deflexão aumentou significativamente a rugosidade dos fios S e STC (p<0,05). A resistência a flexão de FSE e NS (teflon e sem recobrimento, respectivamente) foi maior comparada aos demais grupos (p<0,05). Conclui-se que a rugosidade e resistência a flexão não dependem do tipo de revestimento estético, mas é influenciada pelo modo de aplicação deste revestimento. A deflexão pode aumentar a rugosidade de alguns fios estéticos.

Effect of Acid Etching, Silane and Thermal Cycling on the Bond Strength of Metallic Brackets to Ceramic

Abstract The aim of this study was to evaluate the effect of silanes, thermal cycling and acid etching on the shear bond strength (SBS) of metallic brackets to feldspathic ceramic. Feldspathic ceramic cylinders (Groups 1, 2, 5 and 6) were etched for 60 s with 10% hydrofluoric acid and Groups 3, 4, 7 and 8, without acid etching. Two layers of silane Clearfil Ceramic Primer (CCP, Groups 1 to 4) and two layers of RelyX Ceramic Primer (RCP, groups 5 to 8) were applied and dried for 60 s. Brackets were bonded to the cylinders with Transbond XT and light-activated for 40 s with Bluephase G2. All specimens were stored in deionized water at 37 °C for 24 h, and the specimens of groups 1, 3, 5 and 7 were submitted to 7,000 thermal cycles (5 °C/55 °C). After storage, the SBS test was performed at a crosshead speed of 1 mm/min. Data were subjected to three-way ANOVA and Tukey's post hoc test (α=0.05). The adhesive remnant index (ARI) was evaluated at 8x magnification. The SBS of CCP was significantly greater than of RCP (p<0.05), with or without thermal cycling. Thermal cycling significantly reduced the SBS (p<0.05). The groups submitted to acid etching showed significantly higher SBS than those without acid etching (p<0.05). In conclusion, thermal cycling reduced SBS for all groups. The best ceramic surface treatment for bracket bonding was achieved by acid etching and CCP silane. The ARI results showed predominance of score 0 for all groups.

Resumo O objetivo neste estudo foi avaliar o efeito de diferentes silanos, ciclagem térmica e condicionamento ácido na resistência da união ao cisalhamento (RUC) de bráquetes metálicos a cerâmica feldspática. Cilindros da cerâmica feldspática (Grupos 1, 2, 5 e 6) foram condicionados por 60 s com ácido hidrofluorídrico a 10% e os Grupos 3, 4, 7 e 8 sem condicionamento ácido. Duas camadas do silano Clearfil Ceramic Primer (CCP, Grupos 1 a 4) e duas camadas do RelyX Ceramic Primer (RCP, Grupos 5 a 8) foram aplicadas e secas por 60 s. Bráquetes foram fixados aos cilindros cerâmicos usando Transbond XT e fotoativado por 40 s com Bluephase G2. Todas as amostras foram armazenadas em água deionizada a 37 °C por 24 h, sendo as amostras dos grupos 1, 3, 5 e 7 submetidas a 7.000 ciclos térmicos (5 °C/55 °C). Após a armazenagem, a RUC foi verificada a velocidade de 1 mm/min. Os dados foram submetidos à ANOVA 3 fatores e teste de Tukey post hoc (α=0,05). O Índice de Remanescente do Adesivo (IRA) foi avaliado com aumento de 8x. A RUC do CCP foi significantemente maior do que o RCP (p<0,05), com ou sem ciclagem térmica. A ciclagem térmica reduziu significantemente a RUC (p<0,05). Os grupos submetidos ao condicionamento ácido mostraram valores de RUC significantemente maiores em relação os grupos sem condicionamento ácido (p<0,05). Concluindo, a ciclagem térmica reduziu a RUC para todos os grupos. O melhor tratamento de superfície da cerâmica para colagem de bráquetes foi obtido pelo condicionamento ácido e pelo silano CCP. O IRA mostrou predominância de escore 0 para todos os grupos.

Effect of Polymerization Cycles on Gloss, Roughness, Hardness and Impact Strength of Acrylic Resins

Abstract The aim of this study was to evaluate the conventional and boiled polymerization cycles on gloss, roughness, hardness and impact strength of acrylic resins. Samples were made for each Classico and QC-20 materials (n=10) in dental stone molds obtained from rectangular metallic matrices embedded in metallic flasks. The powder-liquid ratio and manipulation of the acrylic resins' were accomplished according to manufacturers' instructions and the resins were conventionally packed in metallic flasks. After polymerization by (1) conventional: 74 °C for 9 h (Classico) and (2) boiled: 20 min (QC-20) cycles, the samples were deflasked after cooling at room temperature and conventionally finished and polished. The properties were evaluated after storage in water at 37 °C for 24 h. Gloss was verified with Multi Gloss 268 meter (Konica Minolta), surface roughness was measured with Surfcorder SE 1700 rugosimeter (Kosaka), Knoop hardness number was obtained with HMV-200 microdurometer, and impact strength was measured in an Otto Wolpert-Werke device by Charpy system (40 kpcm). Data were subjected to Student's t-test (at α=0.05). The results were: Gloss: 67.7 and 62.2 for Classico and QC-20 resins, respectively; Surface roughness: 0.874 and 1.469 Ra-µm for Classico and QC-20, respectively; Knoop hardness: 27.4 and 26.9 for Classico and QC-20, respectively; and Impact strength: 37.6 and 33.6 kgf/cm2 for Classico and QC-20, respectively. No statistically significant difference (p>0.05)were found between the resins for the evaluated properties. In conclusion, conventional and boiled polymerization cycles had similar effects on gloss, roughness, hardness and impact strength of both Classico and QC-20 resins.

Resumo O propósito neste estudo foi avaliar os ciclos de polimerização convencional e por fervura sobre o brilho, rugosidade, dureza e resistência ao impacto de resinas acrílicas. Amostras foram confeccionadas para cada resina Clássico ou QC-20 (n=20) em moldes de gesso obtidos de matrizes metálicas retangulares incluídas em muflas metálicas. A proporção monômero/polímero das resinas e manipulação foram de acordo com as recomendações dos fabricantes e a massa convencionalmente incluída em muflas metálicas. Após polimerização nos ciclos (1) convencional: 74 °C por 9 horas (Clássico) e (2) fervura: 20 min (QC-20), as amostras foram demufladas após esfriadas em temperatura ambiente e convencionalmente acabadas e polidas. As propriedades foram avaliadas após armazenagem das amostras em água a 37 °C por 24 h. O brilho foi verificado com medidor Multi Gloss 268 (Konica Minolta), a rugosidade avaliada com rugosímetro Surfcorder SE 1700 (Kosaka), a dureza Knoop foi obtida com microdurômetro HMV-200 (Shimadzu) e a resistência ao impacto determinada pelo sistema Charpy (Otto Wolpert Werke). Os dados submetidos ao teste t de Student (α=0.05) mostraram que Os resultados foram: brilho: 67,7 e 62,2 para Clássico e QC-20, respectivamente; rugosidade: 0,874 e 1,469 Ra-µm para Clássico e QC-20, respectivamente; dureza: 27,4 e 26,9 para Clássico e QC-20, respectivamente; e resistência ao impacto: 37,6 e 33,6 kgf/cm2 para Clássico e QC-20, respectivamente. Não houve diference estatisticamente significante entre as resinas para as propriedades avaliadas. Conclui-se que os ciclos de polimerização convencional e por fervura promoveram similares efeitos sobre o brilho, rugosidade, dureza e resistência ao impacto para ambas as resinas Clássico e QC-20.

Influence of Light Source, Thermocycling and Silane on the Shear Bond Strength of Metallic Brackets to Ceramic

The objective of this study was to evaluate the effects of different light sources, thermocycling and silane on the bond strength of metallic brackets to ceramic. Cylinders of feldspathic ceramic were etched with 10% hydrofluoric acid for 60 s. Half of the cylinders (Groups 1 to 4) received two layers of silane. Metallic brackets were bonded to the cylinders using Transbond XT and divided into 8 groups (n=20), according to light source (Radii Plus LED - 40 s; Groups 1, 2, 5 and 6 and XL 2500 halogen light - 40 s; Groups 3, 4, 7 and 8) and experimental conditions with (Groups 2, 4, 6 and 8) without thermocycling (Groups 1, 3, 5 and 7). Shear bond testing was carried out after 24 h of deionized water storage (Groups 1, 3, 5 and 7) and thermocycling (Groups 2, 4, 6 and 8; 7,000 cycles - 5°/55 °C). Date were submitted to three-way ANOVA and Tukey's post hoc test (α=0.05). The Adhesive Remnamt Index (ARI) was evaluated at 8× magnification. The application of silane was effective in increasing the shear bond strength of the brackets to ceramic (p<0.05). Significant difference (p<0.05) on the bond strength was observed between light sources with or without thermocycling. The ARI showed a predominance of scores 0 for all groups, with an increase in scores 1, 2 and 3 for the silane groups. In conclusion, silane improved significantly the shear bond strength of the brackets to ceramic. The thermocycling and light sources influence on the bond strength.

Resumo O objetivo neste estudo foi avaliar o efeito de diferentes fontes de luz, termociclagem e silano na resistência de união de bráquetes metálicos a cerâmica feldspática. Cilindros de cerâmica feldspática foram condicionados com ácido fluorídrico a 10% por 60 s. Metade dos cilindros (Grupos 1 a 4) recebeu duas camadas de silano. Bráquetes metálicos foram colados aos cilindros usando Transbond XT (3M Unitek), formando 8 grupos (n=20), dependendo das fontes de luz usadas para fotoativação (Radii Plus LED - 40s; Grupos 1, 2, 5 e 6 e XL 2500 halógena - 40 s; Grupos 3, 4, 7 e 8), nas condições experimentais com (Grupos 2, 4, 6 e 8) e sem ciclagem térmica (Grupos 1, 3, 5 e 7). O ensaio de resistência ao cisalhamento foi realizado após armazenagem por 24 h em água deionizada (Grupos 1, 3, 5 e 7) ou armazenados e submetidos a ciclagem térmica (Grupos 2, 4, 6 e 8; 7.000 ciclos - 5° e 55° C). Os dados foram submetidos à Análise de Variância de três fatores e teste de Tukey (α=0,05). O Índice de Remanescente Adesivo (IRA) foi avaliado com aumento de 8×. O uso do silano foi efetivo no aumento da resistência de união ao cisalhamento de bráquetes à cerâmica. Diferença significante na resistência de união foi observada entre as fontes de luz, e com ou sem ciclagem térmica. O IRA mostrou predominância de escore 0 para todos os grupos, com aumento de escores 1, 2 e 3 para os grupos com silano. Em conclusão, a aplicação do silano melhorou significativamente a resistência de união ao cisalhamento de bráquete à cerâmica. A ciclagem térmica e as fontes de luz influenciaram a resistência da união.

Influence of Water Storage and Bonding Material on Bond Strength of Metallic Brackets to Ceramic

Abstract: This study investigated the influence of water storage (24 h and 6 months), and Transbond XT and Fuji Ortho LC bonding materials on the bond strength of metallic brackets bonded to feldspathic ceramic. Four cylinders of feldspathic ceramic were etched with 10% hydrofluoric acid for 60 s. Each cylinder received two layers of silane. Metallic brackets were bonded to the cylinders using Transbond XT or Fuji Ortho LC. Light-activation was carried out with 40 s total exposure time using Bluephase G2. Half the specimens for each bonding materials (n=20) were stored in distilled water at 37 °C for 24 h and the other half for 6 months. Shear bond strength testing was performed after storage times at a crosshead speed of 1 mm/min. The adhesive remnant index (ARI) was used to evaluate the amount of adhesive remaining on the ceramic surface at ×8 magnification. Data were subjected to two-way ANOVA and Tukey's test (p<0.05). Transbond XT showed significantly higher bond strength (p<0.05) than Fuji Ortho LC. Significant differences in bond strength (p<0.05) were found when 24 h and 6 months storage times were compared between materials. ARI showed a predominance of score 0 for all groups, and higher scores at 1, 2 and 3 for 24 h storage time. In conclusion, storage time and bonding materials showed significant influence on the bond strength of brackets to ceramic.

Resumo: Este estudo investigou a influência da armazenagem em água (24 h e 6 meses) e dos materiais para colagem Transbond XT e Fuji Ortho LCO na resistência da união de bráquetes metálicos fixados a cerâmica feldspática. Quatro cilindros de cerâmica foram condicionados com ácido fluorídrico a 10% por 60 s. Todos os cilindros receberam duas camadas de silano. Bráquetes metálicos foram fixados aos cilindros utilizando os materiais Transbond XT ou Fuji Ortho LC. A fotoativação foi realizada com tempo de exposição total de 40 s utilizando Bluephase G2. Metade das amostras de cada material de colagem (n=20) foi armazenada em água destilada a 37 °C por 24 h e outra metade por 6 meses. O ensaio de resistência da união ao cisalhamento foi realizado após os períodos de armazenagem à velocidade de 1 mm/minuto. O Índice de Remanescente Adesivo (IRA) foi utilizado para avaliar a quantidade de adesivo residual na superfície da cerâmica, em lupa estereoscópica com aumento de 8x. Os dados foram submetidos à Análise de Variância de dois fatores e teste de Tukey (p<0,05). Transbond XT apresentou resistência de união significativamente maior do que Fuji Ortho LC. Diferença significante (p<0,05) na resistência da união foi encontrada entre os períodos de armazenagem, qualquer que fosse o material para colagem. O IRA mostrou predominância de escore 0 para todos os grupos, com aumento de escores 1, 2 e 3 para o período de armazenagem de 24 h. Em conclusão, o período de armazenagem e os materiais de colagem influenciaram significativamente a resistência da união de bráquetes à cerâmica.

Resistência de união ao esmalte com aplicação do adesivo na base do braquete / Shear bond strength to enamel after application of adhesive on the mesh of brackets

O objetivo deste estudo foi verificar o efeito da aplicação do adesivo na base do braquete, na resistência de união ao cisalhamento ao esmalte bovino. Um total de 160 incisivos bovinos foi condicionado com ácido fosfórico a 37% durante 30 segundos, e o adesivo Transbond XT Primer foi aplicado na base de retenção de 80 braquetes Edgewise para incisivo central superior, enquanto que nos demais braquetes as resinas compostas Transbond XT, Natural Ortho, Tetric Ceram e Z100 foram aplicadas diretamente na base de retenção. As amostras foram armazenadas em água a 37°C durante 24 horas e submetidas ao ensaio de resistência de união ao cisalhamento (RUC) em uma máquina de ensaio universal Instron 4411, com velocidade de 1,0 mm/min. Em seguida, foi avaliado o índice de remanescente adesivo (IRA). Os dados de RUC foram submetidos à Anova 2 fatores e teste de Tukey (α=0,05). A aplicação do Transbond XT Primer na base dos braquetes aumentou significativamente a RUC das resinas Transbond XT, Natural Ortho e Z100, mas diminuiu significativamente a RUC da Tetric Ceram. A maior RUC foi apresentada pela resina Transbond XT. Sem adesivo, a Tetric Ceram demonstrou RUC significativamente maior do que a Z100 e a Natural Ortho. Com adesivo na base do braquete, ocorreu o inverso. A adição do adesivo nos braquetes aumentou as falhas adesivas. Concluiu-se que a aplicação do adesivo na base dos braquetes é indicada para melhorar a união entre a resina e os braquetes...

The aim of this study was to investigate the effect of application of adhesive in the mesh of brackets on bond strength to enamel. One hundred and sixty bovine incisors were acid etched with 37% phosphoric acid for 30s. The adhesive system Transbond XT Primer was applied to the etched enamel and photo activated by LED Ultralume 5 for 10s. Resin composites Transbond XT, Natural Ortho, Tetric Ceram and Z100 were used to bond brackets to enamel. In the half of the sample adhesive Transbond XT Primer was applied to the mesh of brackets before bonding. Shear bond strength was evaluated after 24 h in a universal testing machine Instron 4411 at 1.0 mm/min crosshead speed. The adhesive remnant index (ARI) was evaluated after shear bond strength test. Data were submitted to two-way Anova and Tukey’s test (α=0.05). The use of adhesive in the mesh of brackets significantly increased the bond strength of Transbond XT, Natural Ortho and Z100; however, Transbond XT Primer applied in the mesh of bracket significantly decreased the bond strength of Tetric Ceram. Transbond XT showed significantly the highest shear bond strength. Transbond XT Primer increased the adhesive failures. It can be concluded that the use of adhesive in the mesh of brackets is a good alternative to improve the bond strength of resin to bracket...

Avaliação da resistência ao cisalhamento e miniflexão de resinas ortodônticas associadas ao primer / Evaluation of the shear bond and mini flexural strength of the orthodontics resins associated with primer

O objetivo desse estudo foi avaliar o efeito da aplicação do primer na resina na resistência ao cisalhamento e flexão em compósitos para colagem ortodôntica. Foram colados braquetes em 60 pré-molares humanos com as resinas Orthobond (G1), Z100 (G2) e Transbond XT (G3). Nos grupos 1, 2 e 3 a colagem foi feita de modo convencional, com a aplicação do primer na superfície condicionada. Nos grupos 4, 5 e 6 o primer foi aplicado na resina presente no braquete. Para o teste de flexão, nos grupos 1, 2 e 3 foram confeccionadas barras com as resinas Orthobond, Z100 e Transbond XT sem misturar com o primer. Nos grupos 4, 5 e 6 o primer foi aplicado nas resinas durante a confecção das barras. Os ensaios de resistência ao cisalhamento e flexão de três pontos foram realizados em máquina Instron com velocidade de 1,0 mm/minuto. Os resultados foram submetidos à Anova dois fatores e ao teste de Tukey (α=0,05). Os resultados mostraram que o Transbond XT apresentou resistência ao cisalhamento significativamente maior do que os outros materiais, e que não houve diferença significante quanto ao método de aplicação do primer. No teste de flexão, a resina Orthobond apresentou resistência significativamente menor do que os outros materiais, e a adição do primer reduziu significativamente a resistência à flexão dos materiais. Concluiu-se que a adição do primer na resina reduziu a resistência à flexão dos materiais e não alterou a resistência de união de braquetes ao esmalte. Dentre as resinas, o melhor desempenho foi apresentado pela Transbond XT...

The aim of this study was to evaluate the effect of primer application in shear bond and flexural strength of composite for orthodontic bonding. Brackets were bonded in 60 human premolars with Orthobond (G1), Z100 (G2) and Transbond XT (G3). In groups 1 to 3 the bond was done in a conventional manner with the application of the primer in the etched surface. In groups 4 to 6 the primer was applied on the primer resin in this bracket. For the flexural test, in groups 1-3 bars were made with the Orthobond, Z100 and Transbond XT without mixing with the primer. In groups 4 to 6 primer was applied to the resin during the manufacture of the bars. Shear bond test and flexural three points test were performed in Instron machine with a speed of 1.0 mm/minute. The results were submitted to Anova two factors and Tukey's test (α=0.05). The results showed that Transbond XT showed significantly higher shear bond resistance than the other materials; there was no significant difference in the primer application method. In the flexural test, the resin Orthobond showed significantly lower resistance than the other materials; adding the primer significantly reduced the flexural strength of the materials. It is concluded that the addition of the primer resin reduced the flexural strength of the material and did not alter the bond strength of brackets to enamel. Among the resins, the best performance was presented by Transbond XT...